6101 aluminum is a 6000-series aluminum alloy: there is significant alloying with both magnesium and silicon, and the alloy is formulated for primary forming into wrought products. 6101 is the Aluminum Association (AA) designation for this material. In European standards, it will be given as EN AW-6101. And A96101 is the UNS number.
| Product Name | 6101 Aluminum |
| Alloy | 6*** aluminum are alloyed with magnesium and silicon, are easy to machine and can be precipitation hardened that not to the high strength that 2000 and 7000 series can reach. |
| Temper | H12,H14,H16,H18,H19 etc. |
| Thickness | 0.1mm to 10mm |
| Width | For coil: 600mm ~ 2000mm, or as customize |
| For sheet: 20mm ~ 2200mm, or as customize | |
| Weight/Coil | As the customer's request |
| MOQ | 3 ton |
| Delivery time | Aound 30 days |
| Payment terms | T/T L/C |
| Container | 20ft: 5898mm(L)*2352mm(W)*2393mm(H) Loading 18-25 tons 40ft:12032mm(L)*2352mm(W)*2393mm(H) Loading 25-27 tons |
| Packing | 3 layers of packing. Inside is craft paper, Middle is water plastic film and outside GI steel sheet to be covered by steel strips |
6101 aluminum is a 6000-series aluminum alloy: there is significant alloying with both magnesium and silicon, and the alloy is formulated for primary forming into wrought products. 6101 is the Aluminum Association (AA) designation for this material. In European standards, it will be given as EN AW-6101. And A96101 is the UNS number.
| Chemical Composition % | ||||||||||
| Si | Fe | Cu | Mn | Mg | Cr | B | Zn | Ti | Residuals | |
| 6101 | 0.3-0.7 | ≤0.50 | ≤0.10 | ≤0.03 | 0.35-0.8 | ≤0.03 | ≤0.06 | ≤0.10 | ≤0.10 | ≤0.10 |
| Mechanical Properties | |||||
| Property | Value | ||||
| Tensile Strength | 90 to 26 MPa | ||||
| Yield Strength | 49 to 240 MPa | ||||
| Elongation | 10 to 25% | ||||
| Shear Strength | 70 to 190 MPa | ||||
Electrical bus bar conductor application for enclosed bus electrical installations.
Aluminium / Aluminum 6101 alloy has good machinability. Oil base lubricant is used to perform machining operations. Carbide or high speed tool steel tooling can be used for machining this alloy.
Aluminium / Aluminum 6063 alloy has good hot or cold form-ability.
Aluminium / Aluminum 6101 alloy can be welded using all standard welding methods. Inert gas arc welding method is the most preferred method for welding this alloy. The strength of the subsequent parts will be reduced when welded in the heat treated condition.
Aluminium / Aluminum 6101 alloy can be cold worked in the aged or annealed conditions.
A: We are a manufacturer, can do OEM and ODM.
A: Yes, we have small samples, like A4 size. You need to provide the grade (ALLOY NUMBER) and temper, thickness, width,length and the quantity.
A: Quality is priority. Our factory has gained SGS authentication. We guarantee the goods out form our factory 100% qualified. And each process, we have very strict operation and arrange 2 technicians to inspect. After the products are finished, we will make the last test to pick up the unqualified products.
A: Generally we accept 30% T/T as deposit and 70% against with B/L copy.
Please fill out the form below (required *), send us a short message, and we will contact you as soon as possible.
Copyright © 2022 Tianjin Century Changsheng Trade Co., Ltd